20% Carbon Fiber Reinforced PA6
Introducing Fiberon PA6-CF20, a cutting-edge filament that combines Nylon 6 with 20% carbon fiber, delivering exceptional performance for a variety of applications. This advanced material is engineered for:
- High Stiffness and Strength: Ideal for rigid functional parts, tooling, fixtures, and prototypes.
- Dimensional Stability: Ensures strong layer adhesion for reliable results.
Engineering Performance After Annealing
Experience remarkable mechanical properties with typical values including:
- Tensile Strength: 109.3 MPa (dry X-Y)
- Young’s Modulus: 8.64 GPa
- Heat Deflection Temperature: Reaches 215°C at 0.45 MPa after proper annealing.
Please note that final-part performance may vary based on design and printing conditions.
Moisture Sensitivity
This filament is moisture-sensitive. To achieve optimal results:
- Dry the Filament: Heat at 100°C for 10 hours before printing.
- Storage Conditions: Keep below 20% relative humidity, ideally in a dry box.
- Avoid Printing Issues: Proper moisture control reduces stringing, bubbles, rough surfaces, and inconsistent extrusion.
Advanced Printer Setup Required
For best results, ensure your printer is set up as follows:
- Nozzle Temperature: 280–300°C
- Build Plate Temperature: 40–50°C
- Hotend Type: All-metal hotend with cooling fan off.
- Printing Speed: Up to