20% Carbon Fiber Reinforced PA6

Experience unparalleled performance with Fiberon PA6-CF20, a cutting-edge filament that combines Nylon 6 with 20% carbon fiber. This innovative material is engineered for:

• High Stiffness and Strength: Ideal for creating rigid functional parts, tooling, fixtures, and prototypes in automotive or industrial applications.
• Dimensional Stability: Ensures precise and reliable results for your projects.
• Strong Layer Adhesion: Promotes durability and integrity in your printed parts.

Engineering Performance After Annealing

Unlock the full potential of your prints with impressive mechanical properties:

• Tensile Strength: Achieve a remarkable 109.3 MPa dry X-Y tensile strength.
• Young’s Modulus: Benefit from an 8.64 GPa Young’s modulus for enhanced rigidity.
• Heat Deflection Temperature: Reach up to 215°C at 0.45 MPa after a 16-hour annealing process at 100°C.

Moisture Control is Key

To ensure optimal printing results:

• Drying Process: Dry the filament at 100°C for 10 hours before use.
• Storage Conditions: Keep below 20% relative humidity, preferably in a dry box.
• Avoid Issues: Proper moisture control minimizes stringing, bubbles, rough surfaces, and inconsistent extrusion.

Advanced Printer Setup Required

For best results, configure your printer as follows:

• Nozzle Temperature: Set between 280–300°C.
• Build Plate Temperature: Maintain at 40–50°C.
• Nozzle