20% Carbon Fiber Reinforced PA6

Experience the exceptional strength and durability of Fiberon PA6-CF20, a cutting-edge material designed for high-performance applications. This innovative filament combines Nylon 6 with 20% carbon fiber, offering:

• High Stiffness & Strength: Ideal for creating rigid functional parts, tooling, fixtures, and prototypes.
• Dimensional Stability: Ensures precision and reliability in your projects.
• Strong Layer Adhesion: Enhances the overall integrity of printed components.

Engineering Performance After Annealing

Unlock superior mechanical properties with typical TDS values including:

• Tensile Strength: 109.3 MPa (dry X-Y)
• Young’s Modulus: 8.64 GPa
• Heat Deflection Temperature: Reaches up to 215°C at 0.45 MPa after proper annealing.

Moisture Management

This filament is moisture-sensitive; therefore, it is crucial to:

• Dry Before Printing: Heat the filament at 100°C for 10 hours prior to use.
• Store Properly: Keep below 20% relative humidity, ideally using a dry box.
• Avoid Printing Issues: Proper moisture control minimizes stringing, bubbles, and rough surfaces.

Advanced Printer Setup Required

To achieve optimal results, ensure your printer setup includes:

• Nozzle Temperature: Set between 280–300°C.
• Build Plate Temperature: Maintain at 40–50°C.
• Nozzle Type: Use an all-metal hotend with the cooling fan off.