20% Carbon Fiber Reinforced PA6

Experience the exceptional strength and durability of Fiberon PA6-CF20, a cutting-edge material that combines Nylon 6 with 20% carbon fiber. Perfect for creating rigid functional parts, tooling, fixtures, and prototypes in automotive or industrial applications.

Key Features:

• High Stiffness & Strength: Offers superior dimensional stability and strong layer adhesion.
• Engineering Performance: Achieves a dry X-Y tensile strength of 109.3 MPa and a Young’s modulus of 8.64 GPa.
• Heat Deflection: Reaches up to 215°C at 0.45 MPa after proper annealing.

Benefits:

• Moisture Control: Ensure optimal performance by drying the filament at 100°C for 10 hours prior to printing. Store below 20% relative humidity for best results.
• Advanced Printer Setup: Utilize a nozzle temperature of 280–300°C and a build plate temperature of 40–50°C for optimal printing conditions.
• Wear-Resistant Nozzle Required: Use a hardened steel or ruby nozzle to withstand the abrasiveness of carbon fiber.

Printing Tips:

• Anneal printed parts at 100°C for 16 hours to enhance heat resistance and dimensional stability.
• Confirm smooth filament routing and unrestricted spool rotation before starting long prints.
• Achieve printing speeds up to 300 mm/s with a properly tuned profile.

This advanced material is designed for professionals seeking high-performance solutions in their projects. Elevate your printing experience with Fiberon PA6-CF20!